DIPPED RADIAL LEAD MULTILAYER CERAMIC CAPACITORS
KVDSeries
RCRoomoHpHlSiaSn2t
AECQ200
High temperature
150℃
◆FEATURES
1. Temperature range : -55 to +150℃ 2. Temperature characteristic : X8L 3. Small in size and wide capacitance range.
Max. 15µF is available. 4. Epoxy resin(UL94 V-0)used for coating. 5. Automotive grade(AEC-Q200)
◆APPLICATIONS
1. Noise fillter for automotive equipment(ECU etc.) 2. Equipment used in a high temperature environment
◆CONSTRUCTION
Coating Resin
CDeierlaemctircic Termination
Solder (Pb-free) Internal Electrode Lead Wire
◆RATINGS
1. Category Temperature Range 2. Rated Voltage Range 3. Rated Capacitance Range 4. Rated Capacitance Tolerance 5. Temperature Characteristics 6. Rated Ripple Current
-55~+150℃
25, 50, 100 Vdc 0.1~15μF M(±20%)
X8L
See No.5 on the following table
◆SPECIFICATIONS
No.
1 Withstand Voltage
Items
Between Terminals
Terminals to Coating Resin
2 Insulation Resistance
3 Rated Capacitance
Specification No abnormality.
100/CR(MΩ) or 4000(MΩ) whichever is less. Within specified tolerance.
4 Dissipation Factor
5.0% maximum.
Test Condition
250% of rated voltage shall be applied for 5 seconds. (Only 250Vdc products : 475V)
Rated voltage shall be applied for 60±5 seconds at temperature 25±2℃.
Temperature Frequency Voltage
CR≦10µF
CR>10µF
25±2℃
1±0.1kHz
120±12Hz
1±0.2Vrms
0.5±0.2Vrms
As customer requirement, Chemi-Con has submits the test results according to AEC-Q200 for Multilayer ceramic capacitors. Please contact us for more information.
Product specifications in this catalog are subject to change without notice.Request our product specifications before purchase and/or use. Please use our products based on the information contained in this catalog and product specifications.
29 CAT. No. E1002Y
DIPPED RADIAL LEAD MULTILAYER CERAMIC CAPACITORS
KVDSeries
◆SPECIFICATIONS
No. Items
5 Rated Ripple Current
6
High Temperature Exposure(Storage)
7 Temperature Cycle
8 Biased Humidity
9 Operational Life
Terminal 10 Strength
(Leaded)
Tension Bending
11 Mechanical Shock
12 Vibration
13
Resistance to Soldering Heat
14 ESD
15 Solderability
*CR : Rated Capacitance(µF)
Specification
Test Condition
Size code Arms
32 43 55 0.3 0.8 1.0
Appearance : No structural damage such as cracks ΔC/C : ±20% D.F. : 10% maximum I.R.:50/CR(MΩ) or 1000(MΩ)
whichever is less.
10kHz to 1MHz (sine curve) Ripple voltage Vp shall be less than the rated voltage. The surface temperature of MLCC must not exceed the maximum category temperature when the ripple current is applied. Temperature:Max. category temperature±3℃ Time:1000 ±408 hours
Appearance : No visible damage. ΔC/C : ±15% D.F. : To meet the initial specification. I.R. : To meet the initial specification.
Step 1
Temperature(℃)
Min Category temperature ±3
2 Room temperature
3 Max. Category temperature ±3
4 Room temperature
For 1000 cycles
(min)
30±3
3 max.
30±3
3 max.
Appearance : No abnormality. ΔC/C : ±20% D.F. : 10% maximum I.R. : 25/CR(MΩ) or 1000(MΩ)
whichever is less. Appearance : No structural damage such as cracks ΔC/C : ±20% D.F. : 10% maximum I.R. : 50/CR(MΩ) or 1000(MΩ)
whichever is less.
Temperature:85℃±3℃ Humidity:80 ~ 85%RH Voltage:Rated voltage Time:1000 ±408 hours Temperature:Max. category temperature±3℃ Voltage:Rated voltage Time:1000 ±408 hours
No visible damage.
The force applied shall be :
Lead φ(mm) 0.5 max.
Tensile(N) 5
Lead φ(mm) 0.5 max.
Time : 2times.
Bending(N) 2.5
(sec.)
10±1
(kg) 0.25
Appearance : No abnormality. ΔC/C:To meet the initial specification. D.F. : To meet the initial specification.
Appearance : No abnormality. ΔC/C:To meet the initial specification. D.F. : To meet the initial specification.
Appearance : No visible damage. ΔC/C : ±15% D.F. : To meet the initial specification. I.R. : To meet the initial specification. Appearance : No abnormality. ΔC/C:To meet the initial specification. D.F. : To meet the initial specification. I.R. : To meet the initial specification. Min. 75% of surface of the termination shall be covered with new solder.
MIL-STD-202 Method 213 Condition C Peak value:100G Normal duration:6 ms Velocity change:12.3 ft/sec(3.8m/s) Direction and time:3 times each in
X,Y, Z axis. Total 18 times MIL-STD-202 Method 204 Test condition:5G peak Amplitude:1.5mm max. Frequency:10-2000-10Hz(20 minute) Direction and time:12 times each in
X,Y, Z axis. Total 36 times Solder temp.:260±5℃ Dipping Time:10±1s Depth : 1.5 to 2mm
AEC-Q200-002 Connection:Between terminals Direct Contact:8kV(150pF 2000Ω) Times:±1time
Solder Solder Temperature
Dipping Time
Pb Free
245±5℃
2±0.5s
Product specifications in this catalog are subject to change without notice.Request our product specifications before purchase and/or use. Please use our products based on the information contained in this catalog and product specific.