DSM Engineering Plastics
DSM Engineering Plastics – Property Data
Stanyl® TE250F8
Polyamide 46 40% GF Reinforced, flame retardant
Properties Ph...
Description
DSM Engineering Plastics – Property Data
Stanyl® TE250F8
Polyamide 46 40% GF Reinforced, flame retardant
Properties Physical Properties
Density Melting Temperature Thermal Conductivity Mold Shrinkage
(1)
Typical Data
1740 295 0.24 0.2±0.1 / 0.8±0.3 1.2
Unit
Kg/cm C W/K m % %
3
Test Method
ISO 1183 DSM DSM DSM ISO 1110
MD/TD
Humidity Absorption 23C, 50%RH
Mechancal Properties
Tensile Strength Tensile Modulus
(2) (2)
180 2 15000
(4) (4)
MPa % MPa KJ/m KJ/m
2 2
ISO 527-1A ISO 527-1A ISO 527-1A ISO 179-1eA ISO 179-1eA ISO 178 ISO 178
Tensile Elongation
(3)
Charpy Impact Strength Charpy Impact Strength Flexural Strength Flexural Modulus
(5) (5)
23C –40C
10 10 250 13000
MPa MPa
Thermal Properties
HDT @1.80MPa Coeff. Linear Thermal Expansion 20C – 80C MD/TD >285 2/8 C 1/K x 10
-5
ISO 75-A DSM
Electrical Properties
Dielectric Strength Volume Resistivily Surface Resistivily Dielectric Constant 23C, MHz Dissipation Factor 23C, MHz Flammability >30 10 10
15 16
KV/mm W cm W X 10 -3
IEC 243 IEC 93 IEC 93 IEC 250 IEC 250 UL 94
4.0 16 0.75mm V-0
(1) Measured on plaques (80x80x1mm). Depending on molding conditions. (2) Test Speed: Reinforced=5mm/min, Non-reinforced=50mm/min (3) Test Speed: 1mm/min. (4) Notched, Edgewise (5) Test Speed: Reinforced=2mm/min, Non-reinforced=10mm/min 2mm/min.